Material: | Tungten Carbide |
Still deciding? Get samples of US$ 48/kg
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment Methods: |
|
---|---|
Support payments in USD |
Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Tungsten carbide saw tip is used as the tips for the TCT saw blade for cutting all kinds of original wood, hard wood, HDF, MDF, plywood, particle board, laminated board, composite material, grass, aluminum and metals. It can give much more excellent performance than HSS .
PRODUCT NAME | Carbide saw tips used for cutting HDF | |||||||||||||||||
MATERIAL | Co+WC 100%Virgin Raw Materials | |||||||||||||||||
COLOR | Nickel white/Black/Gray | |||||||||||||||||
STANDARD | DIN GB ISO JIS BA ANSI | |||||||||||||||||
USED | Brazed on the wood-working saw blade for cutting HDF |
Grade |
Physical and mechanical properties |
ISO Code |
Applications recommended |
Proposal for welding |
||||||||||||||
Density g/cnV |
Hardness HRA(HV |
TRS Mpa |
||||||||||||||||
YG6 | 14.6-15.0 | ≥90.0 | ≥1800 | K20 | For the cutting of ordinary wood | use resistance welding the remperature should be not too high |
||||||||||||
VG8 | 14.6-14.9 | ≥89.5 | ≥1900 | K30 | For the cutting of ordinary wood,also for aluminum | use resistance welding the remperature should be not too high |
||||||||||||
JX20 | 14.4-14.7 | ≥90.0 | ≥2000 | K20 | For the cutting of ordinary wood | use resistance welding the remperature should be not too high |
||||||||||||
JX25 | 14.3-14.6 | ≥89.5 | ≥2100 | K30 | For the cutting of ordinary wood,also for aluminum | use resistance welding the remperature should be not too high |
||||||||||||
JX5 | 14.6-15.0 | ≥90.5 | ≥1900 | K10 | Applies to the cutting of hard wood,recycling wood and aluminum | use resistance welding the remperature should be not too high |
||||||||||||
JX9 | 14.5-14.9 | ≥90.5 | ≥2000 | K10 | Applies to the cutting of aluminumopperand lesd.non-ferrous |
recommend the high-frequency welding | ||||||||||||
YG6X | 14.7-15.0 | ≥92 | ≥1800 | K10 | Applies to the cutting of the timber | recommend the high-frequency welding |
||||||||||||
JX05 | 14.8-15.1 | ≥93.3 | &2500 | K05 | Applies to the cutting of hard Wood, also can be used for The cutting of soft metal |
recommend the high-frequency welding | ||||||||||||
JX15 | 14.6-15.0 | ≥92.5 | ≥2400 | K05 | Applies to the cutting of mardwood and aluminum |
recommend the high-frequency welding | ||||||||||||
JX35 | 14.9-15.2 | ≥93.5 | ≥2000 | K01 | , Apply to the cutting of plywood, mdf board and sandwich board |
recommend the high-frequency welding | ||||||||||||
JX40 | 12.8-13.2 | ≥90.5 | ≥2000 | P40 | Apply to the cutting of steel |
recommend the high-frequency welding |
LXWXT(mm) | a° |
r° |
B |
|||||||||||||||
L | W | T° | ||||||||||||||||
7.5 | 2.52.83.03.23.43.63.84.04.24.44.55.26.0 | 2.5 | 28 | 70 | 5 | |||||||||||||
7.5 | 2.83.23.53.74.55.05.66.06.5 | 2.4 | 30 | 50 | 0 | |||||||||||||
8.0 | 2.42.82.93.03.13.23.33.13.53.63.83.94.0 | 2.3 | 28 | 70 | 5 | |||||||||||||
8.0 | 4.34.44.54.85.05.25.56.06.88.0 | 2.5 | 28 | 70 | 5 | |||||||||||||
8.0 | 2.83.03.33.53.84.14.24.65.05.25.510.0 | 3 | 25 | 45 | 0 | |||||||||||||
8.5 | 2.83.03.33.43.53.63.84.14.24.34.65.06.0 | 2.5 | 28 | 70 | 5 | |||||||||||||
9.0 | 3.64.34.55.25.5 | 2.7 | 28 | 45 | 5 | |||||||||||||
9.0 | 3.13.33.53.63.84.34.54.75.25.52.86.0 | 2.7 | 28 | 70 | 5 | |||||||||||||
10.0 | 3.43.54.36.5 | 2.5 | 20 | 68 | 0 | |||||||||||||
10.0 | 3.53.73.94.04.34.54.75.05.56.0 | 2.8 | 28 | 70 | 5 |
LXWXT(mm) | a |
r |
B |
|||||||||||||||
L | W | T° | ||||||||||||||||
10.0 | 6.57.07.510.0 | 2.8 | 28 | 70 | 5 | |||||||||||||
10.0 | 3.53.84.34.54.74.85.05.35.45.56 | 3 | 15 | 72 | 0 | |||||||||||||
10.5 | 3.03.53.87.0 | 2.3 | 28 | 70 | 5 | |||||||||||||
10.5 | 3.03.33.43.53.63.84.04.14.34.4 | 2.5 | 28 | 70 | 5 | |||||||||||||
10.5 | 4.54.65.25.56.5 | 2.5 | 28 | 70 | 5 | |||||||||||||
10.5 | 3.03.43.53.63.84.14.34.54.64.7 | 3 | 28 | 70 | 5 | |||||||||||||
10.5 | 4.85.05.35.55.66.06.57.07.514.5 | 3 | 28 | 70 | 5 | |||||||||||||
10.5 | 3.53.94.04.24.34.44.54.64.74.8 | 3.5 | 28 | 70 | 5 | |||||||||||||
10.5 | 5.05.35.55.86.06.57.08.08.59.010.5 | 3.5 | 28 | 70 | 5 | |||||||||||||
10.5 | 3.53.94.04.14.34.54.74.84.95.1 | 3.5 | 39 | 59 | 5 | |||||||||||||
10.5 | 5.56.56.57.09.0 | 3.5 | 39 | 59 | 5 | |||||||||||||
10.5 | 4.14.85.05.56.06.57.58.59.511.0 | 3.5 | 30 | 75 | 0 | |||||||||||||
12.0 | 4.54.64.75.15.55.86.06.36.57.0 | 3.5 | 30 | 45 | 10 | |||||||||||||
12.0 | 8.08.51012.517.0 | 3.5 | 30 | 45 | 10 |
LXWXT(mm) | α° |
r° |
B° |
|||||||||||||||
L | W | T° | ||||||||||||||||
12.5 | 4.04.54.85.05.45.55.96.26.36.57.07.510.1 | 3.0 | 28 | 70 | 5 | |||||||||||||
12.5 | 4.85.25.35.46.06.36.56.87.07.5 | 3.5 | 28 | 70 | 5 | |||||||||||||
12.5 | 4.55.05.56.06.36.56.87.07.58.09.512.5 | 4.0 | 30 | 70 | 5 | |||||||||||||
13.0 | 4.04.34.55.05.25.55.86.06.36.5 | 4.0 | 30 | 45 | 5 | |||||||||||||
13.0 | 7.07.58.08.28.59.010.011.013.0 | 4.0 | 30 | 45 | 5 | |||||||||||||
13.0 | 4.44.84.95.25.45.75.86.06.36.5 | 4.0 | 30 | 60 | 5 | |||||||||||||
13.0 | 6.77.07.58.510.0 | 4.0 | 30 | 60 | 5 | |||||||||||||
13.0 | 4.04.54.84.95.05.35.56.06.56.8 | 4.0 | 40 | 60 | 3 | |||||||||||||
13.0 | 7.07.58.08.510.0 | 4.0 | 40 | 60 | 3 | |||||||||||||
13.0 | 5.06.07.08.09.010.012.0 | 5.0 | 35 | 45 | 0 | |||||||||||||
14.5 | 4.04.55.05.56.06.57.07.58.08.59.0 | 4.0 | 30 | 70 | 0 | |||||||||||||
14.5 | 10.011.012.012.213.014.014.215.016.0 | 4.0 | 30 | 70 | 0 | |||||||||||||
14.5 | 16.217.018.019.020.0 | 4.0 | 30 | 70 | 0 | |||||||||||||
15.5 | 8.09.512.013.0 | 5.0 | 30 | 0 | 0 |
Features of cemented carbide saw tips blades
1.Production of 0.4 um ultrafine tungsten carbide.